供应POM M90-44日本宝理标准级高流动 低粘度 共聚物塑胶原料:
| POM M90-44 日本宝理塑料物性数据 |
| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 特性：共聚甲醛，高流动性及短周期。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 基本性能 | 吸水率 | 23℃，24hr | ASTM D-570 | 0.22 | % | ||||||||
| 物理性能 |
|
--- |
|
|
--- | ||||||||
| 比重 | --- | ASTM D-792 | 1.41 | --- | |||||||||
| 机械性能 | 抗拉强度 | --- | ASTM D-638 | 60 | MPa | ||||||||
| 拉伸率 | --- | ASTM D-638 | 60 | % | |||||||||
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa | |||||||||
| 弯曲模量 | --- | ASTM D-790 | 2580 | MPa | |||||||||
|
--- |
|
|
|
|||||||||
| 洛氏硬度 | --- | ASTM D-785 | 80 | M | |||||||||
| 电气性能 | 体积电阻系数 | --- | ASTM D-257 | 1×1014 | Ω.cm | ||||||||
| 表面电阻系数 | --- | ASTM D-257 | 1×1016 | Ω | |||||||||
| 介电击穿强度 | --- | ASTM D-149 | 24 | MV/m | |||||||||
| 热 性 能 | 负荷挠曲温度 | 1.32MPa | ASTM D-648 | 110 | ℃ | ||||||||
| 线膨胀系数 | --- | ASTM D-596 | 10 | ×10-5/℃ | |||||||||
| 燃烧性 | --- | UL 94 | 94HB | --- | |||||||||
POM结晶度高，机械强度、刚性、热变形温度等，熔点低，热稳定性，耐化学腐蚀性，流动特性，加工性优，新开发的产品为超高流动（快速成型），耐冲击和降低模具沉积牌号，也有无机填充，增强牌号。
POM吸水率大于0.2%，成型前应预干燥，POM熔融温度与分解温度相近，成型性较差，可进行注塑、挤出、吹塑、滚塑、焊接、粘接、涂膜、印刷、电镀、机加工、注塑是最重要的加工方法，成型收缩率大，模具温度空高些，或进行退火处理，或加入增强材料（如无碱玻璃纤维）。
POM强度高，质轻、常用建材来代替铜、锌、锡、铅等有色金属， 广泛用于工业机械、汽车、电子电器、日用品、管道及配件、精密仪器等部门。
POM吸水率大于0.2%，成型前应预干燥，POM熔融温度与分解温度相近，成型性较差，可进行注塑、挤出、吹塑、滚塑、焊接、粘接、涂膜、印刷、电镀、机加工、注塑是最重要的加工方法，成型收缩率大，模具温度空高些，或进行退火处理，或加入增强材料（如无碱玻璃纤维）。
POM强度高，质轻、常用建材来代替铜、锌、锡、铅等有色金属， 广泛用于工业机械、汽车、电子电器、日用品、管道及配件、精密仪器等部门。